EPOXY PUTTY

EPOXY RESIN PUTTY

Description         

Solvent free, two component expoxy resin putty contains special fine filler.

Main Purpose    

-For filling up cracks.

-For filling up cavities.

-For leveling uneven concrete.

-For grouting joints between tiles.

-For preparation of surfaces before epoxy paints.

 

Product characteristics        

Epoxy Putty is a thixotropic product, accordingly it is

easy to work with it on walls and on roofs.

Adheres also on iron, wood, masonry, ceramics and epoxy .

Therefore Epoxy Putty can be used also to bond the above mentioned

materials together .After hardening Epoxy Putty gives a high mechanical

strength and a tough elastic character.

Technical  Date           

Viscosity at 20ºC cps                                          Thixotropic

Mix ratio by weight                                             19:2

Specific weight at 20ºC (g/cm3)                       approx. 1.7

Pot life at 10oC  (hours).                                    6

Pot life at 20oC  (hours).                                    2

Pot life at 30oC  (hours).                                    1

Min. hardening temperature oC                       +10

Walkable at 20oC  (hours)                                 24

Thorough hardened at 20oC  (days)                7

Re-workable         (hours)                                   12-24

Adhesion to concrete                                          concrete fracture

Storage life in months at 20oC                         12

Colour                                                                    white

Complies with ASTM C-881-78, ASTM C-579-75

 

Surface preparation  

Cement bound surface must br dry, firm, offer good traction, be free from grout, dust and dirt and additionally free of oil, grease and other impurities which can adversely affect uniform adhesion. If considered necessary, the surface should be sand blasted, flame scaled, milled or ground.

 

Application                

It is recommended to use spatula, steel trowel or putty tools.

Note: On steel or for very high adhesion of the Epoxy Putty we recommend to prime first with Euxit 50.

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EPOXY PUTTY.pdf

EUCO FLOORTOP

INDUSTRIAL FLOORING SYSTEM

Description         

EUCO-FLOPOORT is an industrial flooring system designed for use in the most server conditions. It is resistant to corrosive and oxidizing chemicals with high abrasion resistance, compressive and tensile strength. Heavy traffic , continuous soaking in water, salts, oil, organic and inorganic acids, alkalis and many solvents have little effect on durability.

 

Main purpose     

As high resistant antislip flooring in breweries, bakeries,canneries, chemical factories, dairies, flour mills, hospitals, kitchens, garages, parking, schools, shops, warehouses etc.

Advantages           

- antislip

- waterproof

- resistant to acids and alkalis

- high compressive and flexural strength

- impact resistant for example; it’s used for the front wall of the squash court.

- abrasion resistant

- good freeze - thaw resistant

- not harmed by continuous soaking of grease, oil and water

- high bond strength and low shrinkage

- low maintenance

- easy installation

 

Composition        

EUCO FLOORTOP is a two component product.

EUCO FLOORTOP P (powder) is a powder component with selected, specifically graduated aggregates and pigments.

EUCO FLOORTOP L (liquid) is a special developed liquid component to be used in combination with EUCO FLOORTOP P.

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUCO FLOORTOP.pdf

EUXIT 200

MORTAR BASED ON EPOXY RESIN

SLIP AND CHEMICAL RESISTANCE

Description    

Solvent free three component mortar based on epoxy resin.

Fields of  application       

EUXIT 200 has a wide range of application for:

- New buildings .

- Floor maintenance in industries e.g.

EUXIT 200 gives on old and new concrete floors a very hard surface which is slip resistant -and has a very high chemical resistance.

Therefore EUXIT 200 is recommended for :

- Laboratories

- Chemical plants

 - Aircraft hangars

- Metal finishing plants

- Carparks

Product characteristics        

After hardening EUXIT 200 gives a very high strength and a very high resistance to impact and abrasion.

EUXIT 200 is resistant to spillage of chemicals commonly met within industry, including petrol, fuel oils, alcohol, paraffin, aliphatic hydro-carbons.

EUXIT 200 is weather resistant and nearly free of yellowing .

EUXIT 200 is stable to constant temperatures and temperature changes in the       range from - 30oC to + 70oC heat.Floors made by EUXIT 200 can be cleaned by steam jet

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 200.pdf

EUXIT 210
FLOW-MORTAR

Description         

Solvent free, three compo  nent flow-mortar on epoxy resin

 

Main purpose     

- For the grouting of bearing plates, machine bases, crane runways and bridge abutments.

- For Fixing bolts  anchors and reinforcement.

Product characteri -stics     

EUXIT 210 contains special selected resin, hardener and mineral aggregate which give EUXIT 210 a high fluidity. EUXIT 210 hardens without shrinkage and is resistant to high mechanical loads and to a wide range of aggressive chemicals.

Technical data               

Specific weight           (g/cm3)                       approx. 1,8

Pot life at 10oC           (hours)                         1.8

Pot life at 20oC           (hours)                         2

Pot life at 30oC           (hours)                         1

Min. hardening temperature (oC)                   8

Thorough hardened at 20oC (days)                7

Compressive strength (N/mm2)                      80-100

Bending property (N/mm2)                            approx. 30

Adhesion to concrete                                      concrete fracture

E-module (N/mm2)                                        approx. 104

Storage life in months at 20oC                       6

Complies with ASTM D 2240

C-1181, C-579, D-531, D-543, C-580, C-307, C-884

 

Surface preparation      

Cement bound surfaces must be dry, firm, offer,good traction, and be free from grout, dust and dirt particles, and additionally be free from oil, grease and other impurities which can adversely affect uniform adhesion. If considered necessary, the surface should be sand blasted, flame scaled or ground.

 

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 210.pdf

EUXIT 220

Description           

Solvent free two component epoxy adhesive mortar.

Main purpose    

- For fixing light-shafts.

- For fixing structure elements made of concrete, steel  and wood .

- For repairing edges of stairs ...... etc. .

- For repairing bridge-trusses .

 

Product characterstics         

EUXIT 220 is a thixotropic product, accordingly it is easy to work  -   with it .on walls and on roofs.

EUXIT 220 adheres on concrete, steel and wood. Therefore EUXIT 220 can be used also to bound the above mentioned materials together.

EUXIT 220 is weather resistant and nearly free of yellowing.

EUXIT 220 is high resistant to a wide range of aggressive chemicals commonly used in industry.

EUXIT 220 is unaffected by constant temperatures and temperature changes in the range from -30o to + 100oC dry heat and up to + 50oC wet heat. For short periods the product can withstand temperatures up to 50% higher. 

EUXIT 220 can be cleaned by steam jet.

Technical data       

Viscosity at 20oC cps                                     thixotopic

Mix ratio by volume                                       2 : 1

Mix ratio by weight                                        2 : 1

Specific weight at 20oC (g/cm3)                    1,8

Pot life at 10oC           (hours)                         2 1/2

Pot life at 20oC           (hours)                         1 1/2

Pot life at 30oC           (hours)                         3/4

Min. hardening temperature (oC)                   +8

Walkable at 20oC (hours)                               24

Thorough hardened at 20oC (days)                7

Re-workable   (hours)                                     12-24

Compression strength (N/mm2)                      90

Bending property        (N/mm2)                      35

Thermal expansion oC-1                                45 x 10-6

Adhesion to concrete                                      concrete fracture

Storage life in months at 20oC                       6

Colour                                                             Gray

 

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 220.pdf

EUXIT 222

EPOXY RESIN PUTTY

Description            

Solvent free, two component epoxy resin putty.

 

Main purpose 

- For filling up cracks.- For filling up cavities.

- For repairing edges of stairs  .

- For leveling uneven concrete, for fixing light stressed parts.

- For fixing steel reinforcement into old concrete while repairing R.C.structures.

 

Product Characteri-Stics

EUXIT 222 is a thixotropic product, accordingly it is easy to work with it on walls and on roofs. Adheres also on iron, wood, masonry, ceramics, epoxy and on eternity .Therefore

EUXIT 222 can be used also to bond the above mentioned materials together. After hardening

EUXIT 222 gives a high mechanical strength and a tough elastic character. 

EUXIT 222 is high resistant to a wide range of aggressive chemicals commonly used in industry.

 

Technical data 

Viscosity at 20oC cps                                     thixotropic

Mix ratio by weight                                        19 : 1

Specific weight at 20oC  (g/cm3)                   approx. 1,7

 Pot life at 10oC           (hours)                         6

Pot life at 20oC           (hours)                         2

Pot life at 30oC           (hours)                         1

Min. hardening temperature (oC)                   + 8

Walkable at 20oC  (hours)                              24

Thorough hardened at 20oC (days)                7

Re-workable    (hours)                                     12-24

Compression strength (N/mm2)                      60

Bending property (N/mm2)                            30

E-module at 20oC (N/mm2)                           7500

Adhesion to concrete                          concrete fracture

Storage life in months at 20oC                       6

Colour                                                             Gray

Complies with ASTM C-881-78, ASTM C-579-75

Surface preparation

Cement bound surfaces must be dry, firm, offer good traction, be free from grout, dust and dirt and additionally free of oil, grease and other impurities which can adversely affect uniform adhesion. If considered necessary, the surface should be sand blasted, flame scaled, milled or ground.Iron and steel must be free of rust scales and should be free from oil, dust , grease and other dirt particles. The best method of preparation is to flame scale or sand blast.

 

Application         

It is recommended to use steel spatula and steel trowel.

                       

Note:                     

On steel or for very high adhesion of the EUXIT 222 putty we recommend to prime first with EUXIT 50 or EUXIT 55.

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 222.pdf

EUXIT 230

SELF LEVELING FLOOR TOPPING

Description       

 Solvent free, pigmented, two component, self-leveling epoxy flooring.

Fields of  application  

Abrasion and chemically resistant flooring for cement bound surfaces, such as concrete, floor plaster, asbestos cement, and also for iron and steel.

The main fields of application are floors in dairies, slaughter houses, textile factories, chemical plants, battery plants, power-stations, offices and public buildings industry ....... etc.  .

 

Product Characteri-stics        

EUXIT 230 when properly hardened is very hard and has high resistance to abrasion. It is waterproof, waste and sea-waterproof and shows resistance to alkalis, diluted acids, saline solutions, mineral oils and aliphatic hydrocarbons.

EUXIT 230 is particularly free of yellowing.

EUXIT 230 is unaffected by constant temperatures and temperature changes in the range from -30o to +90o C dry heat and up to 40oC wet heat. For short periods the product can withstand temperatures 20-30% higher. EUXIT 230 can be cleaned by steam jet.

 

Technical data 

Mix ratio (by weight)                                      16 : 1

Mix ratio (by volume)                                     8,75 : 1

Pot life at 10oC           (hours)                         2

Pot life at 20oC           (hours)                         1

Pot life at 30oC           (hours)                         1/2

Minimum hardening temperature (oC)           8

Bone dry at 20oC (hours)                                6

Walkable at 20oC (hours)                               24

Thorough hardened at 20oC (days)                7

Re-workable at 20oC (hours)                          8-24Volume shrinkage (%)                                    1

Linear shrinkage   (%)                                                0,1

Pencil hardness                                               2 H

Erichsen indentation (mm)                              1

Adhesion to concrete after storage

at temperature changes                                   concrete-fracture

E-module (N/mm2)                                         7500

Compression strength (N/mm2)                      approx. 60

Bending property (N/mm2)                            approx. 30

Storage life in months at 20oC                       12

Complies with ASTM D 2240, ASTM D 2047, BS 6319

Surface preparation        

Cement bound surfaces must be dry, firm, offer good traction,be free from grout, dust and dirt and additionally free of oil, grease and other impurities which can adversely affect uniform adhesion. If considered necessary, the surface should be sand blasted, flame scaled, milled or ground.

Application 

Procedure for cement bound surfaces:

Thin smooth coating:

-Prime with EUXIT 50 or EUXIT 55 Material consumption, depending on absorbency of the surface:200-400 g/m2.

-On the next day apply the top coating of EUXIT 230 with a spatula or squeegee to the required coating thickness (min. 2-3 mm), then roll with a spiked roller to remove all air and at the same time level off consumption2-3 liters per m2

-If a especial non-slip surface is desired, immediately sprinkle the paving mixture with sand 0,7 - 1,2 mm approx.

Container      

EUXIT 230 is supplied in drums of 5 liters, 10 liters and 20 sizes   and             liters.Resin and hardener are supplied in correct mix ratios.

colour         102 Light gray            703 Light green

121 Dark gray             705 Dark green

201 Beige                    800 White

302 Brick red              Other colours are available

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 230.pdf

EUXIT 300

ACRYLIC RESIN QUICK MORTAR

Description     

Ready to use two component quick mortar on acrylic resin base.

 

Fields of apationplic          

EUXIT 300 is a ready to use quick mortar especially for repair work of concrete, runways, concrete roads........ etc. ..

 

Product characteri-stics

After hardened EUXIT 300 gives a very high strength and a very high resistance to impact and abrasion.

EUXIT 300 is weather resistant and free of yellowing.

 

Technical data  

Specific gravity                                   2,0

Pot life 10oC                                       30 min.

Pot life 20oC                                       25 min.

pot life 30oC                                       20 min.

 Min. hardening temperature               - 10oC

Thorough hardened                            60 min. /90 N/mm2

Volume shrinkage %                          3

Linear shrinkage %                             0,07

Compression N/mm2                          90

Bending property N/mm2                   35

Adhesion on concrete                         concrete fracture

Storage life in months at 20oC           6

Surface                

Cement bound surfaces must by dry, firm, offer good traction

 

preparation

and be  free from grout, dust and dirt particles, and additionally free of oil grease and other impurities which can adversely affect uniform adhesion. If considered necessary the surface should be sand blasted, flame scaled, faced or ground.

Application

 Processing for repair work :

-Impregnation of the surface with EUXIT 301 a liquid acrylic-resin.

- Pouring of EUXIT 300 .

- If you have a mortar thickness more than 10 cm mix EUXIT 300 with clean, dry gravel or work in different layers.

Container Size and colour   

Packing: 5 x 1 liter

Colour : Gray

 

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 300.pdf

EUXIT 301

ACRYLIC RESIN QUICK MORTAR

Description          

Two component acrylic resin

 

Main purpose           

EUXIT 301 is an impregnation resin for concrete under

EUXIT 300 quick-mortar.

 

Product characteristics        

After proper hardening EUXIT 301 shows  good resistance to acids, alcalyes and chemical solvents and is free of yellowing.

 

Technical data          

Viscosity at 20oC cps                         10 - 30

Specific gravity                                   1,0

Hardening time (hours)                       20oC   2

Flash point                                          10

Surface preparation 

Cement bound surfaces must be dry, firm. Offer good traction, and be free from grout, dust and dirt particles, and additionally be free from oil, grease and other impurities which can adversely affect uniform adhesion. If considered necessary, the surface should be sand blasted. Flame scaled or ground.

 

Application       

EUXIT 301 is applied by roller or brush.

 

Container Size & Colour         

Packing : 1 x 1 liter

Colour : Colourless.

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 301.pdf

EUXIT 302

ACRYLIC RESIN FOR NORMAL AND COLOURED MORTAR

Description    

Solvent free two-component acrylic resin formulated with a peroxide hardener.

 

Main purpose

EUXIT 302 has a wide range of application for

- Flooring of new buildings.

- Floor maintenance.

- Repair edges of stairs ........ etc. .

- Repair bridges and concrete roads.

- Repair walls and machine basements ....... etc. .

- Repair of runways.

 

Product characterstics         

EUXIT 302 gives , whether  filled with our non-pigmented filler or with our pigmented filler, very  high early strength. As the chemical reaction starts already at -10oC, these advantage can be used for instance for repair-work in cool stores.

EUXIT 302 is free of yellowing and shows a very good resistance to acids, alkalis and chemical solvents.

 

Technical data                                                                      

EUXIT 302                                                    EUXIT 302

Gray or coloured mortar ratio                         EUXIT 302/    filler 1:6.

Approx. depending on filler .

Viscosity at 20oC/cps                                     80-100             ---

Specific Gravity at 20oC (g/cm3)                   1,0                   2,0

Potlife at 20oC min.                                        15                    15

Minimum hardening temperature                   -10oC              -10oC

Compressive strength/2 h          N/mm2            ---                    50-60

Compressive strength/2 days    N/mm2 39                                130-150

Tensile bending property           N/mm2            16                    35-40

Tensile strength                         N/mm2            5                      ---

Volume shrinkage                        %                  12                    0,3

 Linear shrinkage                          %                   1,0                   ---

Adhesion on concrete                                   concrete          concrete 

fracture            fracture

Flash point                                 oC                   + 10                 ---

Colour                                                             colourless        gray or

other                                                                colour

Storage life in months at 20oC                       12                    ---

Surface Preparation

Cement bound surfaces must be dry, firm, offer good traction, and be free from grout, dust and dirt particles, and additionally free from of oil, grease and other impurities which can adversely affect uniform adhesion. If considered necessary, the surface should be sandblasted, flame-scaled, milled or ground.

 

Application   

EUXIT 302 is supplied in correct mix ratio (resin/hardener).

Hardener must be thoroughly mixed with the resin. Please consult our technical leaflet with the mixing instructions.

If a mortar has to be made, mix first the resin and hardener and then add filler up to the desired consistency. Mix well resin and filler by using a drilling machine.

EUXIT 302 can be filled up with filler up to a ratio (weight) of 1:6 the applied mortar has to be protected from humidity for 6-8 hours, otherwise the colour of the mortar surface may change to white or the surface may not harden thoroughly.

EUXIT 302 mortar can be applied by trowel.

 

Container Sizes         

Containers of 5 kg / 10 kg / 25 kg / 200 kg available.

container sizes and colour of EUXIT 302 filler Filler in bags 25 kg; standard colour gray for other please contact our sales service.

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 302.pdf

EUXIT 309

ACRYLIC MORTAR

Description    

Solvent free two-component acrylic mortar formulated with a peroxide hardener .

 

Fields of application 

EUXIT 309 has a wide range of application for

- Flooring of new buildings.

- Floor maintenance in industries e.g.

EUXIT 309 gives on old and new concrete floors a very hard surface which is slip and very high chemical resistant.In addition EUXIT 309 is nearly free of yellowing and withstands wet conditions.

EUXIT 309 is recommended for:

- Slaughter houses .

- Cool stores .

- Laboratories.

- Aircraft hangars.

- Car parks.

- Food factories

 

Product characteristics        

EUXIT 309 gives a very high strength. High early strength can be achieved also in cool stores as the chemical reaction starts already at - 10oC.

EUXIT 309 shows very good resistance to acids, alkalis and chemical solvents. It adheres also with iron and steel.

 

Technical data  

Specific gravity at 20oC g/cm3                      2,0

Potlife at 20oC min.                                        15

Minimum hardening temperature                   -10oCCompressive strength /2H      N/mm2                        50-60Compressive strength/2 days N/mm2             130-150

Tensile bending property        N/mm2            35-40

Volume shrinkage            %                            0,3

Adhesion on concrete                                     concrete fracture

Colour                                                             Gray or other                 

Surface preparation 

Cement bound surfaces must be dry, firm, offer good traction and be free from grout, dust and dirt particles, and additionally, be free of oil, grease and other impurities which can adversely affect uniform adhesion. If considered necessary, the surface should be sandblasted, flame-scaled or ground .

 

Application   

EUXIT 309 is supplied in correct mix, resin and hardener/filler. The resin has to be added to the hardener/filler and must be thoroughly mixed. Please

consult our technical leaflet with the mixing instructions.

The applied mortar has to be protected from humidity for 6-8 hours, otherwise the colour of the mortar surface may change to white or the surface may not thorough harden. EUXIT 309 can be applied by trowel.

 

Important : To achieve a proper adhesion we recommend to prime the concrete first with EUXIT 301.

 

Container sizes   and colour            

EUXIT 309 is supplied in containers of

1 Lt. , 10 Lt. 

Gray For other colour please contact our sales service.

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 309.pdf

EUXIT 310

ACRYLIC FLOW-MORTAR

Description    

Solvent free two component acrylic flow-mortar formulated with a peroxide hardener.

 

Main purpose

- For the grouting of bearing plates.

- For the grouting of machine bases.

- For the grouting of crane-runways, bridge abutments.

- For fixing bolts and anchors and reinforcement.

 

Product characteristics        

EUXIT 310 gives very soon a high strength even on temperatures of -10oC. These advantages can be used for instance for repair work in cool stores.

 

Technical data         

Specific weight (g/cm3)                                  2,0

Pot life at 20oC  min.                                      10

 Pot life at 10oC  min.                                      20

 Pot life at 0oC    min.                                      40

Pot life at -10oC min.                                      75

Min. hardening temperature oC                      -10

Compression strength at 20oC

after 2 hours          N/mm2                              50-60

after 2 hours          N/mm2                              130-150

Bending property N/mm2                               35-40

Volume shrinkage in %                                  0,3

Storage life in months at 20oC                       6

Surface preparation 

Cement bound surfaces must be dry, firm, offer good traction, and be free from grout, dust and dirt particles, and additionally be free from oil, grease and other impurities which can adversely affect uniform adhesion. If considered necessary, the surface should be sand blasted, flame scaled, or ground.

 

Application   

Depending on the problem the form-work has be to absolutely leak proof.

For casting the EUXIT 310 care must be taken that all the air is removed out of the admixture.

Big voids can be repaired with EUXIT 310 as follows:

- Fill in the voids dry crushed rocks or gravel approx. 15-30 mm .

- After that , fill continuously the EUXIT 310 over the gravel or crushed rock  into the voids.

The advantages of this procedure are:

- Less tension because of less reaction temperature.

- Less material consumption.

 

Container      

EUXIT 310 is supplied in containers of 5 liters

 

Sizes  and Colour    

Resin and hardener are supplied in correct mix ratios.

Colour : Gray.

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 310.pdf

EUXIT 451

ACRYLIC FLOW-MORTAR

Description    

A solvent contains colourless one component preparation on base of Alkoxysilan.

 

Main purpose

EUXIT 451 is used to impregnate and to seal cement bound  surfaces as a hydrophobic impregnation. To impregnate concrete, plaster, concrete, roads, concrete parking areas, aircraft hangars, industrial floors, petrol stations, terraces and balconies..

 

Product characteristics        

EUXIT 451 has an extremely low viscosity. Because of its high capillary action it forces itself deeply into the foundation material and fills all pores and capillaries. Cement bound surfaces are thereby hydrophobe and sealed against damp, water and water solvent substances. The penetration of steam is impeded, but however, is not completely prevented. The impregnated surfaces are hardened and become resistant to the effects of frost-tha wsalt.

 

Technical data

Specific gravity at 20oC (g/cm3)                    0,8

Solvents                                                          Ethanol

Colour                                                             Colourless

Shelf life in months at 20oC                           min. 12

Storage                                                            well closed, cool

Precautions                                                      flammable liquid

Surface preparation and application         

EUXIT 451 can be sprayed with an airless-gun, applied by roller or brushed on. The surface should be clean and dry to allow a good penetration.

 

Consumption

Depending on the absorbency of the concrete-surface approx. 200-400 g/m2.The total amount should be applied in 1-3 coatings with intervals of about 15 minutes between each (wet on wet).

 

Container Sizes and colour

EUXIT 451 is supplied in containers of 25 liters and 200 liters.

Colour : colourless

 

Precautions

Skin contamination should be immediately cleaned with soap and water. It is recommended, that rubber gloves and glasses be worn whilst working.

This product contains solvents. Therefore when working in enclosed places, good ventilation must be provided . Do not smoke and don't expose to open flames .

 

Typical                       Impregnated with       Without treatmentwith

results                                 EUXIT 451                 EUXIT 451

Diffusion resistant factor          106                              120

Vapor resistance (h/m)             1,32                             1,50

Water absorbing property       0,017                           0,761

(kg/m2/h)                                0,057                           0,471

 

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 451.pdf

EUXIT 455

ANTI-GRAFFITI PROTECTION COAT

Description    

EUXIT 455 is a ready to use, solvent containing one component preparation to impregnate and to seal cement based surface and natural stones.

 

Main purpose             

EUXIT 455 is used to impregnate and to seal cement bound surfaces and natural stones as a hydrophobe impregnation. It is specially used to protect buildings, monuments, metro-stations, railway-stations a.s.o. against painting by vandals. EUXIT 455 is an "Antigraffiti coat". Such painting can easily be removed by washing the surface .

 

Product characteristics        

EUXIT 455 has an extremely low viscosity. Because of his high capillary action it forces itself deeply into the foundation material and fills all pores and capillaries. The surfaces are thereby hydrophobe and sealed against paint, sprayed or brushed on.

 

Technical data

Specific gravity                                   1,3

Flash point                                          over 50oC

Solvent                                                trichlorethane

Colour                                                 colourless

Storage                                                well closed, cool

Precautions                                          flammable

 

Application data       

EUXIT 455 can be applied with roller, brush or by spray equipment.The surface must be dry, clean and free of dust, oil etc. EUXIT 455 is invisible, but due to the adsorption of the substrate a small colour change may occur (we recommend to test the colour change).The fresh painted surface should be protected against rain for 24 hours.As EUXIT 455 contains solvents, when working in closed places good ventilation must be provided. Do not smoke and no open flame.Skin contamination should be immediately cleaned with soap and water. It is recommended, that rubber gloves and glasses be worn whilst working.The solvents of EUXIT 455 may dissolve bitumen, sealant, paints .....etc. Therefore joints, paints etc. has to be protected while EUXIT 455 is applied.

 

Consumption

Depending on absorbency of the substrate:

Concrete          300-400 g/m2

Normal stone  300-600 g/m2

The total amount should be applied in one coat without intervals, so that a continuous penetration is given (wet on wet).

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 455.pdf

EUXIT 500

CLEANER

Description    

Mixture of organic-chloride-solvents.

 

Main Purpose             

To clean all tools which has been used to work

with EUXIT resin products.

 

Product characteristics        

EUXIT 500 is a flammable organic cleaner. Hardener and not hardened epoxy and acrylic-resins can be dissolved with EUXIT 500.

 

Instruction for use   

Tools which has been not immediately cleaned can be put for 12-24 hours in EUXIT 500. After this procedure has been done for use brush the rest of resin together with EUXIT 500 of  F.

Remarks        

EUXIT 500 is flammable !

 

Container sizes

Packing : 1x 5 litters.

 

Physiological Reactions and precautions

EUXIT 500 is caustic. Therefore it is absolutely  essential that the skin does not come into contact with the hardener. It is recommended that rubber gloves be worn whilst working. Skin contamination should be immediately cleaned with soap and plenty of water, better still with an addition of  2% household vinegar. If splashed into the eyes, they should immediately be washed with plenty of water. By means of an eye bath with boric acid, (obtainable from chemists and pharmacies) rinse out, and then report immediately to an eye specialist. At all times local statutory safety regulations with regard to working with epoxy hardeners and the handling of solvents should be strictly observed.

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 500.pdf

EUXIT 501

THINNER FOR EUXIT-PRODUCTS

Description    

Mixture of organic-chloride-solvents.

 

Main purpose

EUXIT 501 is a special thinner for EUXIT products.

 

Product characteristics        

EUXIT 501 reduces the viscosity of EUXIT products.

There for the advantages are:

- Easy to brush .

- Easy to roll .

- Easy to spray .

- Better penetration into the concrete therefore better adhesion of EUXIT 80 .

 

Instructions for use

EUXIT 501 can be given directly to the final mixture of EUXIT products (component I + component II ) or separate to component I and component II.Mixing EUXIT 501 to EUXIT products we recommend to use a drilling or boring machine with a whirl. While adding the EUXIT 501 the speed of the machine should be approx. 300 r.p.m.

Remarks 

EUXIT 501 is flammable!

 

Container sizes   

Packing 1 x 5 liters

 

Physiological reactions and precautions    

EUXIT 501 is caustic. There fore it is absolutely essential that the skin does not come into contact with the hardener. It is recommended that rubber gloves be worn whilst working. Skin contamination should be immediately cleaned with soap and plenty of water, better still with an addition of 2 % household vinegar. If splashed into the eyes, they should immediately be washed with plenty of water. By means of an eye bath with boric acid, (obtainable from chemists and pharmacies) rinse out, and then report immediately to an eye specialist. At all times local statutory safety regulations with regard to working with epoxy hardeners and the handling of solvents should be strictly observed.

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT 501.pdf

EUXIT TB 50

ELASTIC COATING MATERIAL

FOR CONC., ASPHALT, IRON, STEEL & TIMBER

Description    

A solvent free, two component preparation on tar-polyurethane base (Poly-mixture with iscoyanate hardener).

 

Fields of  application      

EUXIT TB 50 is a very elastic coating material for concrete, asphalt, iron and steel timber, especially for coating roadways and floors such as, for example, steel surfaced roads, temporary roadways, mastic asphalt roads, industrial asphalt floors, wooden bridges and similar constructions. 

Especially suitable for re-conditioning and repair of asphalt roads and bridges.

 

Properties      

When properly hardened EUXIT TB 50 is a tough, highly elastic product, and is highly resistant to abrasion and is non-skid. It is resistant to diluted chemicals and saline solutions and also to aliphatic hydrocarbons, petrol,        heating oil, brake-fluids and similar substances. EUXIT TB 50 can withstand constant temperatures in region of minus 30 to plus 100o C dry heat, and up to plus 60oC wet heat.

 

Technical data     

Viscosity 8 mm Din at 20oC (sec)                  60 - 80

 Specific gravity at 20oC (g/m3)                      1,2

Mix ratio (by weight)                                      5 : 1

Mix ratio (by volume)                                     5 : 1

Pot life at 10oC  (hours)                                  1,5

Pot life at 20oC  (hours)                                  3/4

Pot life at 30oC  (hours)                                  1/4

Minimum hardening temperature (C) 3

Bone dry at 20oC  (hours)                               2

Walkable at 20oC  (hours)                              24

Thorough hardened at 20C (aft.days) 4

Water absorption aft. 21 days at 23oC

a) Regul. test: 50x50x1 mm (weight %)         0,6

b) Din. 53472 test: 50x50x4 mm (weight %) 0,15

Weight loss aft. 28 days at 60°C

a) test thickness: 0,3 mm (weight %) 7,5

b) test thickness: 4 mm (weight %)                0,8

Volume shrinkage (%)                                    4

Linear shrinkage (%)                                      0,3

Shore A hardness                                            70

E-module                                            approx. 50 kp/cm3

max. joint movement (%)                               3-5

 

Instructions for use   

EUXIT TB 50 is supplied in correct mix ratios. The

hardener (com.B) is poured into the base component A care must be taken to ensure that the hardener is completely emptied from its container.

Mixing of the two components is best effective by means of a mechanical stirrer at a max. of 300 r.p.m. (a slowly revolving boring machine fitted with a whirl). Mix thoroughly! Ensure that at the sides and on the base the hardener is uniformly distributed in all directions. The mixture must be stirred until it becomes homogenous. The temperature of both components  should be 10-20 oC when mixing together. The material must not be applied directly from the original storage container: After mixing, the product should            be poured into a shallower container and again carefully mixed.

EUXIT TB 50 can be applied by roller, brushed on, or applied by dented spatula ,squeegee or wiper blade. To remove air bubbles, the surface should be gone over with a spiked roller.

 

Surface preparation           

Cement bound surfaces must be dry, firm, offer good  traction , be free from grout, dust and dirt, and. Additionally, by free of oil, grease and other impurities which can adversely affect uniform adhesion. If necessary, the surface should be sand blasted, flame scaled, milled or ground.

Iron and steel must be free of rust and scale and should be free from oil, dust, grease and other impurities which can adversely affect uniform adhesion.

Best surface-preparation is flame-scaling or sand-blasting.

Asphalt must be firm, dry, free of loose particles, free of dust, oil and grease.

In addition, 75% of the aggregate (granulation) should lay free on the top surface. If necessary, mill or blast.

1- Coating procedure for cement bound surfaces.

Surface coating compound, smooth or non-skid, for coating thickness of  2-4 mm .

1.1 Prepare surfaces as above .

1.2 Prime with EUXIT TB 50

Material consumption, depending on surface absorption, 200-400 g/m2.

1.3 Immediately after applying the primer, sprinkle with fire dried quartz sand 0,2-0,7 mm micron.

Consumption of sprinkled granulation, approx. 1,5 kg/m2.

1.4 After an interval of 1 day, apply the surface coating compound, which should comprise of :

1 part (volume) EUXIT TB 50

1,5 parts (volume) fire dried quartz and 0,2-0,7 mm

micron thoroughly mix the EUXIT TB 50 (components A and B), then immediately stir in the sand .Pour the mixture and spread to required thickness with a dented spatula or squeegee, and then roll with a spiked roller to 

eliminate air bubbles and level off.

Material consumption 600 g EUXIT TB 50 50/m2and mm thickness.

1.5 If a non-skid surface is required, immediately sprinkle with the fire dried quartz sand 0,7-1,2 mm micron.

Consumption of granulation approx. 4 kg/m2.

2- Coating procedure for iron and steel.

2.1 Sand blast according to rost 2.213 (optimum peak to valley depth

approx. 50) .

2.2 Prime with EUXIT TB 50 .

Material consumption. approx. 300-500 g/m2, depending on

temperature.

2.3 If further work cannot be undertaken within 5 hours, then the fresh primer should be sprinkled with fire dried quartz sand 0,2-0,7 mm.

Consumption of sprinkled granulation 2 kg/m2.

2.4 1-5 hours after applying the primer, or alternatively 24 hours after

sprinkling with sand, apply the surface coating compound which should comprise of the following:-

1 part (volume) EUXIT TB 50 .

1 part (volume) fire dried quartz sand 0,2-0,7 mm micron

1/2 part (volume) calculated bauxite 1-3 mm.

This material should be applied to a thickness of approx. 4 mm.

Material consumption, approx. 2 kg EUXIT TB 50 /m2.

2.5 Immediately after applying the surface coating compound ,

sprinkle with calcinated bauxite 1 - 3 mm or 2 - 5 mm micron after sprinkling , it is worth while to roll in the bauxite with a light roll .

3- Coating procedure for asphalt.

3.1 Coating to improve the traction of asphalt roads .

3.1.1 Prepare surface as above.

3.2.2 Prime with EUXIT TB 50 .

Material consumption approx. 400 g/m2.

3.2.3 If further work cannot be undertaken within 5 hours,

immediately sprinkle the freshly applied primer with fire dried quartz sand, granulation 0,2 -0,7 mm  Consumption of sprinkled granule,

1,5-2 kg/m2.

3.2.4 1-5 hours after applying the primer, or 24 hours after the sand

has been sprinkled, apply the surface coating compound, which should comprise of the following:-

1 part (volume) EUXIT TB 50 .

1 part (volume) fire dried quartz sand 0,2-0,7 mm micron and

1/2 part (volume) calcinated bauxite 1-3 mm or fire gravel 1-3 mm

micron. This material should be applied to a coating thickness of app.

4-5 mm.  Material consumption, approx. 2 kg EUXIT TB 50 /m2.

3.2.5 Immediately after applying the surface coating, sprinkle with calcinated  bauxite 1-3 mm or 2-5 mm or alternatively fine gravel 1-3 mm or 2-5 mm micron.

3.2.5 Immediately after applying the surface coating compound, sprinkle with calcinated bauxite 1-3 mm or 2-5 mm micron.

After sprinkling, it is worth while to roll in the bauxite with a light

roller. For track re-conditioning and coating over 1 cm it is worth

while to apply the surface coating compound in two coatings, whereby

the first surface coating compound should be made up of:-

1 part (volume) EUXIT TB 50 .

1 part (volume) fire dried quartz sand 0,2-0,7 mm.

1-2 parts (volume) fine gravel 2-5 mm to be added.

The above described fine mortar should be applied on top of this

coarse surface compound .

 

Cleaning  and appliances     

All tools and appliances should be thoroughly washed and cleaned

with Tools EUXIT TB 50 universal thinner immediately after use!

 Physiological reactions and precautions in use

After proper hardening EUXIT TB 50 physiologically harmless. As a

tar containing product, however, it is not permitted to be used for component B (hardener) contains isocyanate and is caustic. Care must be taken so that the hardener does not come into contact with the skin, especially not with the eyes and mucous membranes. It is

recommended that rubber gloves be worn whilst working. Skin contamination should be immediately cleaned with soap and plenty of water, better still with an addition of 2% household vinegar.

If splashed into the eyes. They should immediately be washed with plenty of water. By means of an eye bath with boric acid, (obtainable from chemists and pharmacies), rinse out, and then report immediately to an eye specialist. At all times local statutory safety regulations with regard to working with epoxy hardeners should be strictly observed.

 

Container sizes and col. shades      

EUXIT TB 50 is supplied in containers of 5 kg and 12 kg. Resin and

hardener are supplied in correct mix ratio

Color : Black.

 

Storage 

Both components of EUXIT TB 50 are separately packed have a storage life of at least 12 months. After longer periods of storage, reactibility can decrease. Store in a cool and dry place!

The foregoing information is based on our own research and practical experience and is intended to be guidance to the end user. The information is compiled from scientific findings. We recommend that a check be made to a certain that this product is suitable for use under existing local conditions, and if necessary, a test coating should be made. We cannot be held liable for consequences deriving from this technical specification.

Our general conditions of supply and terms of payment are applicable.

Your web browser doesn't have a PDF plugin. Instead you can download it by clicking the file below

EUXIT TB 50.pdf